Tailoring Vapor-Phase Fabrication of Mn3O4 Nanosystems: From Synthesis to Gas-Sensing Applications

Supported p-Type α-Mn3O4 nanosystems were fabricated by means of chemical vapor deposition (CVD) on polycrystalline alumina substrates at temperatures of 400 and 500 °C, using Mn(hfa)2·TMEDA (hfa = 1,1,1,5,5,5-hexafluoro-2,4-pentanedionate; TMEDA = N,N,N′,N′-Tetramethylethylenediamine) as precursor compound. The structure, chemical composition, and morphology of the obtained deposits were characterized in detail, devoting particular attention to the influence of the used reaction atmosphere (dry O2 vs O2 + H2O) on the system characteristics. For the first time, the gas-sensing performances of the obtained CVD Mn3O4 nanomaterials were investigated toward ethanol and acetone vapors, with concentrations ranging from 10 to 50 and from 25 to 100 ppm, respectively. The developed systems showed the best activity ever reported in the literature for Mn3O4 chemoresistive sensors in the detection of the target gases, a result that, along with their low detection limits and good selectivity, is an appealing starting point for eventual technological applications.