2019
Abstract:
The effect of solution treatment on an AlSi3Mg alloy with and without Cr and Mn addition was investigated. Beside the modification of the morphology of Fe-containing intermetallics, Cr and Mn allowed the formation of dispersoids in the aluminium matrix after solution heat treatment, as shown by scanning transmission electron microscope (STEM) observations. These particles were responsible of enhanced Vickers microhardness of the aluminium matrix in comparison with the base alloy due to dispersion hardening mechanism. Furthermore, a slow heating rate enhanced uniform distribution of dispersoids, as shown by STEM observation, and it leaded to an increase in the material hardness
Tipologia CRIS:
4.1 Contributo in Atti di convegno
Keywords:
Aluminum alloys; dispersion hardening; electron microscopy; solution treatment; Vickers hardness; Materials Science
Elenco autori:
Tocci, Marialaura; Pola, Annalisa; Angella, Giuliano; Donnini, Riccardo; Vecchia, Giovina Marina La
Link alla scheda completa:
Titolo del libro:
Materials Today: Proceedings
Pubblicato in: