The development and understanding of self-healing mechanisms have been investigated in blends of ionomers (Poly(ethyelene-co-methacrylic acid), sodium & zinc ions) (EMNa & EMZn) containing both elastomers (Epoxidized natural rubbers (ENR) and cis-1,4-Polyisoprene (PISP)) and crystalline component (Poly(vinly alcohol-co-ethylene) [PVAcE]) as secondary phases. All the blends were prepared by melt-blending and self-healing behavior was studied in ballistic puncture tests. Self-healing behavior of each material was evaluated by observing the impact zones under a stereo-optical microscope and the micrographic results were further supported by the fluid flow test in the punctured zones. Interestingly, ENR50 blends of sodium ion containing ionomers exhibited complete self-repairing behavior while zinc ion containing ionomer showed limited mending but EMNa/ENR25 and EMNa/PISP blends did not show any self-healing behavior following the damage. On the other hand, a composition dependent healing behavior was observed in the EMNa/PVAcE blends where healing was observed up to 30wt% PVAcE containing blends. The chemical structure studied by FTIR analysis showed that both ion content of ionomer and functionality of ENR have significant influence on the self-repairing behavior of blends. TEM analysis revealed that self-healing occurs in the blends when the dispersed phase has a dimension of 100 to 400 nm.